javad64
06-08-2010, 04:12 AM
Hello
Do you know any reference that if we want to know when recommended to use special material ? ( i.e. A106 for high temp. & A53 for usual temp. or 1.4571 for line contain acid ) I read steel key & ASTM FERROUS MATERIAL but can not find useful thing .
Thank you

FATHI
06-23-2010, 09:47 PM
..go and see Bednar Book , Pressure vessels Handbook

You can find this book in this site

There is a dedicated chapter about material selection ..very clear

You have first to start when selecting a material by determinaing the MINImum metal design temperature ,
Read also ASTM A20 to know some limitations.....etc

javad64
06-25-2010, 02:43 PM
..go and see Bednar Book , Pressure vessels Handbook

You can find this book in this site

There is a dedicated chapter about material selection ..very clear

You have first to start when selecting a material by determinaing the MINImum metal design temperature ,
Read also ASTM A20 to know some limitations.....etc
Hello
Thank you my friend .
I search but can not find ASTM A20 .
can you upload it for me ?
I have another question in below link and if you can help me I grateful you .

FATHI
06-26-2010, 08:38 AM
Hello

I have another question in below link and if you can help me I grateful you .


Ok Done ..go and see the answer

Salam